Emperol Colours Pvt. Ltd.
|
|
VALUE ADDITION WITHOUT EXCEPTATION
|
|
|
|
|
|
|
|
|
|
|
Product description
|
Product Composition
|
Apprx.
|
Recomm.
|
TCC * at
|
Mixing
|
Overcoating
|
|
|
|
Volume
|
Dry Film
|
Recomm.
|
Ratio by
|
Interval
|
|
|
|
solids
|
Thickness
|
DFT
|
Volume
|
Min.
|
Max.
|
|
|
|
(%)
|
(Microns)
|
(m2/l)
|
( B : H ) $
|
(hours)
|
( days )
|
|
Em-Guard ( Anti-corrosive Epoxy Primers )
|
|
31 - ZINC RICH ( 90 )
|
Two-component, air drying, epoxy zinc rich primer
|
48
|
25-50
|
19 -10
|
3 : 1
|
16
|
Unlimited
|
|
|
with 90-92 % zinc dust on dry film
|
|
|
|
|
|
|
|
38 - ZINC RICH ( 80 )
|
Two-component, air drying, epoxy zinc rich primer
|
40
|
25-50
|
16-8
|
3 : 1
|
16
|
Unlimited
|
|
|
with 90-92 % zinc dust on dry film
|
|
|
|
|
|
|
|
32 - R O SHOP PRIMER
|
Two-component, air drying, epoxy-polyamide red
|
43
|
25-35
|
17-12
|
4 :1
|
16
|
30
|
|
|
oxide zinc chromate primer.
|
|
|
|
|
|
|
|
32 - Z P PRIMER GREY
|
Two-component, air drying, epoxy-polyamide
|
43
|
25-35
|
17-12
|
4 :1
|
16
|
30
|
|
|
zinc phosphate primer grey
|
|
|
|
|
|
|
|
33 - H B Z P PRIMER
|
Two-component, polyamide cured, air drying, epoxy
|
50
|
35-50
|
14-10
|
4 : 1
|
16
|
30
|
|
|
zinc phosphate primer grey
|
|
|
|
|
|
|
|
Em-Guard ( Anti-corrosive Epoxy Rust Tolerant Coating )
|
|
35 - SELF PRIME
|
Two-component, high build, rust incapsulating,
|
80-85
|
100-150
|
8 - 5
|
2 : 1
|
16
|
30
|
|
MASTIC - ALUMINIUM
|
modified epoxy aluminium coating.
|
|
|
|
1.24 k:0.485
|
|
|
|
37 - COAL TAR EPOXY
|
Two-component, high build, rust incapsulating,
|
65
|
100-150
|
6.5 - 4.3
|
3 : 1
|
16
|
5
|
|
|
modified tar epoxy coating.
|
|
|
|
|
|
|
|
Intermidiate Coat
|
|
Em-Guard 34 - HB MIO
|
Two-component, high build, epoxy polyamide with
|
60
|
75-100
|
8 – 5
|
3 : 1
|
24
|
30
|
|
GREY
|
micaceous iron oxide pigment.
|
|
|
|
|
|
|
|
Epoxy Flooring
|
|
Em-Flor Primer
|
Two-component, high build, epoxy polyamide Primer
|
100
|
-
|
-
|
2 : 1
|
12
|
30
|
|
Em-Flor SLF (1 kit)
|
Four component Epoxy Self Leveling Flooring
Consisting of Resin-R + hardner-H + color paste-CP + Aggrigates-AG
|
100
|
-
|
10sq. mt / kit / 1mm thickness
|
R = 4 kg
H = 2.3 kg
CP = 250gm
AG = 8 kg
|
1-2 days for lt. load
7 days for heavy load traffic
|
Ask for tech. bulletin
|
|
Epoxy finish paint.
|
|
EP-4 Epoxy Enamel.
|
Two-component, epoxy polyamide having extremely tough, high performance coating with outstanding chemical resistance decorative enamel.
|
35-40
|
35-40
|
9 -10
|
4 : 1
|
24
|
40
|
|
CHLORINATED RUBBER PAINTS (C.R.)
|
|
|
Em-Clor 74 ZP Primer Grey
|
C.R. based anticorrosive primer containing Zn Phosphate as a corrosion inhibiting pigment
|
30
|
40-50
|
6-7
|
-
|
2
|
-
|
|